搜索结果: 1-15 共查到“矿床学与矿相学 Removal”相关记录32条 . 查询时间(0.156 秒)
A Novel MnOx Supported Palygorskite SCR Catalyst for Lower Temperature NO Removal from Flue Gases
Ammonia TPD Low-Temperature SCR Manganese Oxides Palygorskite
2011/11/14
Palygorskite supported manganese oxide catalysts (MnOx/PG) were prepared for lower temperature selective catalytic reduction (SCR) of NOx by NH3. Catalyst’s SCR activity was estimated at varied temper...
The Effect of Thermal Treatment on the Structure of Palygorskite Used for Flue Gas SO2 Removal
Palygorskite SO2 Thermal Treatment
2011/11/14
Palygorskite is widely used as industrial adsorbent and also potential for flue gas desulfurization by adsorption of SO2. The effect of thermal treatment on Palygorskite’s structural properties and it...
Removal of Cd(II) from Aqueous Solution by Electrospun Nylon 6 Nanofibrous Nonwoven Containing Attapulgite
Adsorption Attapulgite Electrospun Fiber Nylon 6
2011/11/15
The attapulgite powders modified by silicane coupling agent are loaded onto the surface of nylon 6 nanofibers by immersing the nylon 6 electrospun fiber nonwoven in a bath containing modified attapulg...
Removal of Cu(II) Ions from Aqueous Solution by KH-570 Modified Attapulgite Clay
Adsorption Copper Ion Modified Attapulgite Clay (ATP) by KH-570
2011/11/15
Attapulgite clay (ATP) was modified by Silane coupling agent (KH-570) to creat more efficient sites for Cu(II) adsorption. The natural and KH-570 modified attapulgite clay were characterized by Fourie...
Adsorptive Removal of 2,6-Dichlorophenol from Aqueous Solution by Surfactant-modified Palygorskite Sorbents: Equilibrium, Kinetics and Thermodynamics
Chemistry Tribology Adsorption and Surface Science Palygorskite Sorbents
2011/11/8
Raw palygorskite was modified by the addition of selected surfactants, viz. hexadecyltrimethylammonium bromide (CTAB), cetylpyridinium bromide (CPB) and octadecyldimethylbenzyl ammonium chloride (ODBA...
Removal of radiocobalt from aqueous solution by oxidized MWCNT
Removal Co(II) Oxidized MWCNT Sorption
2011/11/11
The study was undertaken to evaluate the feasibility of oxidized multiwalled carbon nanotube (oxidized MWCNT) for the removal of radiocobalt (60Co) from aqueous solutions. The oxygen functional groups...
Fast removal of ammonium ion using a hydrogel optimized with response surface methodology
Adsorption Ammonium ion Box–Behnken design Hydrogel Response surface methodology
2011/12/14
Response surface methodology (RSM) based on a three-level, three-variable, Box–Behnken design (BBD) was used to optimize the preparation parameters of a hydrogel consisted of polyvinyl alcohol (PVA),a...
Removal of Chromium (VI) in Tannery Wastewater by Immobilized Technology
Bacillus cereus Chromium (VI) Immobilisation Tannery Wastewater
2011/12/21
Bacillus cereus was embedded in powdered activated carbon to prepare immobilized granule. Then, the granules was used to treat the Cr(VI) in tannery wastewater. The results showed the removal effect o...
Effect of biotite content of hydrogels on enhanced removal of methylene blue from aqueous solution
Hydrogel Biotite Methylene blue Adsorption equilibrium Kinetics
2011/12/14
A series of chitosan-g-poly(acrylic acid)/biotite (CTS-g-PAA/BT) hydrogels with unique clay biotite (BT) were prepared and used to remove cationic dye methylene blue (MB) from aqueous solution by batc...
Rapid removal of Pb(II) from aqueous solution by chitosan-g-poly(acrylic acid)/attapulgite/sodium humate composite hydrogels
composite hydrogels adsorption Pb(II) attapulgite sodium humate
2011/10/10
A series of novel granular chitosang-poly(acrylic acid)/attapulgite/sodium humate (CTSg-PAA/APT/SH) composite hydrogels were successfully prepared by one-step free radical graft polymerization and app...
Arsenic Removal from Wastewater Using Adsorptive Mediums
Adsorptive Capacity Adsorptive Medium BV HFO-PDR Recyclability
2011/11/22
Different adsorptive mediums and adsorbents’ compounds were chosen to remove arsenic from Yangzonghai Lake wastewater. Results showed that Ca(OH)2, attapulgite, bentonite, LDHs these adsorptive medium...
Response surface methodology was employed to optimize the adsorption parameters of Methylene Blue onto a chitosan-g-poly(acrylic acid)/halloysite hydrogel composite with 50% halloysite content. Such o...
Removal of Pb(II) from Aqueous Solution Using Composite Filter Material Made of Fly Ash
Adsorption Composite Filter Material Fly Ash (FA) Pb(II)
2011/11/22
Adsorption of Pb(II) on composite filter material mainly made of fly ash was investigated for the removal of Pb(II) from aqueous solution. Batch experiments have been carried out for adsorption of Pb(...
Fast removal of methylene blue from aqueous solution by adsorption onto chitosan-g-poly (acrylic acid)/attapulgite composite
Composites Attapulgite Chitosan Adsorption Methylene blue
2011/12/13
Batch adsorption experiments were carried out for the removal of methylene blue (MB) cationic dye from aqueous solution using chitosan-g-poly (acrylic acid)/attapulgite composites (CTS-g-PAA/APT) as a...
Removal of Cd(II) from aqueous solution by a composite hydrogel based on attapulgite
composite hydrogel attapulgite cadmium adsorption mechanism thermodynamic parameters
2011/10/10
Chitosang-poly(acrylic acid)/attapulgite composite with 30 wt% attapulgite content was used to remove Cd(II) from aqueous solutions. The parameters influencing the adsorption were investigated. When C...